點擊圖片查看大圖Rynite® 415HP NC010
THERMOPLASTIC POLYESTER RESIN
PET-I-GF15
CHARACTERISTICS
Regional availability
- Global
Processing
Injection Molding
Delivery form
Pellets
Additives
Release agent
PRODUCT TEXT
Common features of Rynite® thermoplastic polyester include mechanical and physical properties such as excellent balance of strength and stiffness, dimensional stability, creep resistance, heat resistance, high surface gloss and good inherent electrical properties at elevated temperature. It can be processed over a broad temperature range and has excellent flow properties.
Rynite® thermoplastic polyester resins are typically used in demanding applications in the automotive, electrical and electronics, appliances where they successfully replace metals and thermosets, as well as other thermoplastic polymers.
Rynite® 415HP NC010 is a 15% glass reinforced, toughened modified polyethylene terephthalate resin improved for easy, fast processing over a broad molding range.
PRODUCT INFORMATION
VALUE
TEST NORM
Resin Identification
PET-IGF15
ISO 1043
Part Marking Code
>PET-IGF15<
ISO 11469
RHEOLOGICAL PROPERTIES
VALUE
UNIT
TEST NORM
Molding shrinkage, parallel
0.3
%
ISO 294-4, 2577
Molding shrinkage, normal
0.8
%
ISO 294-4, 2577
Molding shrinkage, parallel, annealed
0.5
%
ISO 294-4
Molding shrinkage, normal, annealed
1.2
%
ISO 294-4
Postmolding shrinkage, normal, 48h at 175°F
0.35
%
ISO 294-4
Postmolding shrinkage, parallel, 48h at 175°F
0.1
%
ISO 294-4
MECHANICAL PROPERTIES
VALUE
UNIT
TEST NORM
Tensile Modulus
4700
MPa
ISO 527-1/-2
Stress at break
79
MPa
ISO 527-1/-2
Strain at break
5
%
ISO 527-1/-2
Flexural Modulus
3550
MPa
ISO 178
Compressive strength
90
MPa
ISO 604
Shear Strength
40
MPa
ASTM D 732
Charpy impact strength, 73°F
55
kJ/m2
ISO 179/1eU
Charpy impact strength, -22°F
25
kJ/m2
ISO 179/1eU
Charpy notched impact strength, 73°F
11
kJ/m2
ISO 179/1eA
Charpy notched impact strength, -22°F
8
kJ/m2
ISO 179/1eA
Izod notched impact strength, 73°F
13
kJ/m2
ISO 180/1A
Izod notched impact strength, -22°F
7.7
kJ/m2
ISO 180/1A
Hardness, Rockwell, M-scale
58
-
ISO 2039-2
Hardness, Rockwell, R-scale
111
-
ISO 2039-2
Poisson's ratio
0.36
-
-
THERMAL PROPERTIES
VALUE
UNIT
TEST NORM
Melting temperature, 18°F/min
250
°C
ISO 11357-1/-3
Temp. of deflection under load, 260 psi
207
°C
ISO 75-1/-2
Temp. of deflection under load, 65 psi
235
°C
ISO 75-1/-2
Vicat softening temperature, 90°F/h, 11 lbf
205
°C
ISO 306
Coeff. of linear therm. expansion, parallel
20
E-6/K
ISO 11359-1/-2
Coeff. of linear therm. expansion, normal
120
E-6/K
ISO 11359-1/-2
Coeff. of linear therm. expansion, Normal, -40-23°C
40
E-6/K
ISO 11359-1/-2
Coeff. of linear therm. expansion, Normal, 55-160°C
32
E-6/K
ISO 11359-1/-2
Coeff. of linear therm. expansion, Parallel, -40-23°C
98
E-6/K
ISO 11359-1/-2
Coeff. of linear therm. expansion, Parallel, 55-160°C
109
E-6/K
ISO 11359-1/-2
Eff. thermal diffusivity
9E-8
m2/s
-
RTI, electrical, 30mil
140
°C
UL 746B
RTI, electrical, 60mil
140
°C
UL 746B
RTI, electrical, 120mil
140
°C
UL 746B
RTI, impact, 30mil
120
°C
UL 746B
RTI, impact, 60mil
120
°C
UL 746B
RTI, impact, 120mil
120
°C
UL 746B
RTI, strength, 30mil
140
°C
UL 746B
RTI, strength, 60mil
140
°C
UL 746B
RTI, strength, 120mil
140
°C
UL 746B
FLAMMABILITY
VALUE
UNIT
TEST NORM
Burning Behav. at 60mil nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
UL recognition
yes
-
UL 94
Burning Behav. at thickness h
HB
class
IEC 60695-11-10
Thickness tested
0.75
mm
IEC 60695-11-10
UL recognition
yes
-
UL 94
Oxygen index
19
%
ISO 4589-1/-2
Glow Wire Flammability Index, 30mil
700
°C
IEC 60695-2-12
Glow Wire Flammability Index, 40mil
700
°C
IEC 60695-2-12
Glow Wire Flammability Index, 60mil
700
°C
IEC 60695-2-12
Glow Wire Flammability Index, 80mil
725
°C
IEC 60695-2-12
Glow Wire Flammability Index, 120mil
775
°C
IEC 60695-2-12
Glow Wire Ignition Temperature, 30mil
675
°C
IEC 60695-2-13
Glow Wire Ignition Temperature, 40mil
675
°C
IEC 60695-2-13
Glow Wire Ignition Temperature, 60mil
675
°C
IEC 60695-2-13
Glow Wire Ignition Temperature, 80mil
700
°C
IEC 60695-2-13
Glow Wire Ignition Temperature, 120mil
725
°C
IEC 60695-2-13
FMVSS Class
B
-
ISO 3795 (FMVSS 302)
Burning rate, Thickness 1 mm
33
mm/min
ISO 3795 (FMVSS 302)
ELECTRICAL PROPERTIES
VALUE
UNIT
TEST NORM
Relative permittivity, 100Hz
4.5
-
IEC 62631-2-1
Relative permittivity, 1MHz
3.9
-
IEC 62631-2-1
Dissipation factor, 100Hz
654
E-4
IEC 62631-2-1
Dissipation factor, 1MHz
236
E-4
IEC 62631-2-1
Volume resistivity
1E11
Ohm*m
IEC 62631-3-1
Surface resistivity
1E13
Ohm
IEC 62631-3-2
Electric strength
38
kV/mm
IEC 60243-1
Comparative tracking index
350
-
IEC 60112
Comparative tracking index
2
PLC
UL 746A
OTHER PROPERTIES
VALUE
UNIT
TEST NORM
Humidity absorption, 80mil
0.25
%
Sim. to ISO 62
Water absorption, 80mil
2.5
%
Sim. to ISO 62
Density
1390
kg/m3
ISO 1183
INJECTION
VALUE
UNIT
Drying Recommended
yes
Drying Temperature
120
°C
Drying Time, Dehumidified Dryer
4 - 6
h
Processing Moisture Content
≤0.021
%
Melt Temperature Optimum
285
°C
Min. melt temperature
270
°C
Max. melt temperature
290
°C
Max. screw tangential speed
0.2
m/s
Mold Temperature Optimum
95
°C
Min. mold temperature
75
°C
Max. mold temperature
95
°C
Hold pressure range
≥80
MPa
Hold pressure time
4
s/mm
Back pressure
As low as possible
MPa
Ejection temperature
170
°C
1: At levels above 0.02%, strength and toughness will decrease, even though parts may not exhibit surface defects.