點(diǎn)擊圖片查看大圖美國LNP POM芳綸增強(qiáng) KA000M 自潤滑POM
LNP LUBRICOMP KA000M is a compound based on Acetal Copolymer resin containg Aramide and Proprietary Lubricant. Added features include Internally Lubricated.
LNP LUBRICOMP KA000M是一種基于含有芳綸和專用潤滑劑的縮醛共聚物樹脂的化合物。附加功能包括內(nèi)部潤滑。
KA000M物性表：
| 葉生 13925706091 | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, break, 5 mm/min | 60 | MPa | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 8.8 | % | ISO 527 | |
| Flexural Stress, break, 2 mm/min | 64 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 | |
| IMPACT | ||||
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m2 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A | |
| THERMAL | ||||
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 135 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Mold Shrinkage on Tensile Bar, flow | 1.4-2.2 | % | SABIC method | |
| Wear Factor Washer | 8 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified: Manual | |
| Dynamic COF | 0.23 | - | ASTM D 3702 Modified: Manual | |
| Static COF | 0.21 | - | ASTM D 3702 Modified: Manual | |
| Density | 1.37 | g/cm3 | ISO 1183 | |
| INJECTION MOLDING | ||||
| Drying Temperature | 80 | °C | ||
| Drying Time | 4 | hrs | ||
| Melt Temperature | 200-215 | °C | ||
| Front - Zone 3 Temperature | 210-220 | °C | ||
| Middle - Zone 2 Temperature | 195-205 | °C | ||
| Rear - Zone 1 Temperature | 175-190 | °C | ||
| Mold Temperature | 80-110 | °C | ||
| Back Pressure | 0.2-0.3 | MPa | ||
| Screw Speed | 30-60 | rpm | ||