防火抗紫外線ABS FR15U NA1000 美國沙伯基礎
FR15U NA1000
Flame retardant ABS. Excellent indoor UV properties. Excellent moldability. UL94V-0/5VA rated. Elevated UL RTI rating.
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 37 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 30 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 2.4 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 17 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 2060 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 67 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 50 mm/min | 41 | MPa | ISO 527 | |
| Tensile Strain, break, 50 mm/min | 22.0 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2210 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 63 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2260 | MPa | ISO 178 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 213 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 28 | J | ASTM D 3763 | |
| Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m2 | ISO 180/1A | |
| THERMAL | ||||
| Vicat Softening Temp, Rate B/50 | 93 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 86 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 75 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 9.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 9.18E-05 | 1/°C | ASTM E 831 | |
| Vicat Softening Temp, Rate B/50 | 92 | °C | ISO 306 | |
| Relative Temp Index, Elec | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.19 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method | |
| Melt Flow Rate, 230°C/3.8 kg | 3.3 | g/10 min | ASTM D 1238 | |
| Melt Viscosity, 200°C, 1000 sec-1 | 3200 | Poise | ASTM D 3825 | |
| Density | 1.19 | g/cm3 | ISO 1183 | |
| Melt Flow Rate, 220°C/5.0 kg | 7 | g/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 40 | cm3/10 min | ISO 1133 | |
| ELECTRICAL | ||||
| Arc Resistance, Tungsten {PLC} | 7 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 4 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 1 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+14 | Ohm-cm | IEC 60093 | |
| Dielectric Strength, in oil, 3.2 mm | 20 | kV/mm | IEC 60243-1 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94V-0 Flame Class Rating | 1.49 | mm | UL 94 | |
| UL Recognized, 94-5VA Flame Class Rating | 2.79 | mm | UL 94 | |
| INJECTION MOLDING | ||||
| Drying Temperature | 80-90 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Drying Time (Cumulative) | 8 | hrs | ||
| Maximum Moisture Content | 0.1 | % | ||
| Melt Temperature | 205-230 | °C | ||
| Nozzle Temperature | 205-230 | °C | ||
| Front - Zone 3 Temperature | 205-220 | °C | ||
| Middle - Zone 2 Temperature | 200-210 | °C | ||
| Rear - Zone 1 Temperature | 170-180 | °C | ||
| Mold Temperature | 50-70 | °C | ||
| Back Pressure | 0.3-0.7 | MPa | ||
| Screw Speed | 30-60 | rpm | ||
| Shot to Cylinder Size | 50-70 | % | ||
| Vent Depth | 0.038-0.051 | mm |