Rynite® 545 NC010
THERMOPLASTIC POLYESTER RESIN
PET-GF45
CHARACTERISTICS
Regional availability
- Global
Processing
Injection Molding
Delivery form
Pellets
Additives
Release agent
PRODUCT TEXT
Common features of Rynite® thermoplastic polyester include mechanical and physical properties such as excellent balance of strength and stiffness, dimensional stability, creep resistance, heat resistance, high surface gloss and good inherent electrical properties at elevated temperature. It can be processed over a broad temperature range and has excellent flow properties.
Rynite® thermoplastic polyester resins are typically used in demanding applications in the automotive, electrical and electronics, appliances where they successfully replace metals and thermosets, as well as other thermoplastic polymers.
Rynite® 545 NC010 is a 45% glass reinforced modified polyethylene terephthalate resin.
PRODUCT INFORMATION
VALUE
TEST NORM
Resin Identification
PET-GF45
ISO 1043
Part Marking Code
>PET-GF45<
ISO 11469
RHEOLOGICAL PROPERTIES
VALUE
UNIT
TEST NORM
Viscosity number
55
cm3/g
ISO 307, 1157, 1628
Molding shrinkage, parallel
0.2
%
ISO 294-4, 2577
Molding shrinkage, normal
0.8
%
ISO 294-4, 2577
Postmolding shrinkage, normal, 48h at 175°F
0.35
%
ISO 294-4
Postmolding shrinkage, parallel, 48h at 175°F
0.05
%
ISO 294-4
MECHANICAL PROPERTIES
VALUE
UNIT
TEST NORM
Tensile Modulus
15500
MPa
ISO 527-1/-2
Stress at break
182
MPa
ISO 527-1/-2
Strain at break
2
%
ISO 527-1/-2
Flexural Modulus
13500
MPa
ISO 178
Compressive strength
230
MPa
ISO 604
Shear Strength
50
MPa
ASTM D 732
Tensile creep modulus, 1h
15600
MPa
ISO 899-1
Tensile creep modulus, 1000h
13300
MPa
ISO 899-1
Charpy impact strength, 73°F
60
kJ/m2
ISO 179/1eU
Charpy impact strength, -22°F
40
kJ/m2
ISO 179/1eU
Charpy notched impact strength, 73°F
11
kJ/m2
ISO 179/1eA
Charpy notched impact strength, -22°F
11
kJ/m2
ISO 179/1eA
Izod notched impact strength, 73°F
11
kJ/m2
ISO 180/1A
Hardness, Rockwell, M-scale
100
-
ISO 2039-2
Hardness, Rockwell, R-scale
120
-
ISO 2039-2
Poisson's ratio
0.33
-
-
THERMAL PROPERTIES
VALUE
UNIT
TEST NORM
Melting temperature, 18°F/min
252
°C
ISO 11357-1/-3
Temp. of deflection under load, 260 psi
226
°C
ISO 75-1/-2
Temp. of deflection under load, 1200 psi
180
°C
ISO 75-1/-2
Vicat softening temperature, 90°F/h, 11 lbf
230
°C
ISO 306
Coeff. of linear therm. expansion, parallel
15
E-6/K
ISO 11359-1/-2
Coeff. of linear therm. expansion, normal
83
E-6/K
ISO 11359-1/-2
Thermal conductivity solid
0.32
W/(m K)
-
Eff. thermal diffusivity
1.4E-7
m2/s
-
RTI, electrical, 30mil
140
°C
UL 746B
RTI, electrical, 60mil
140
°C
UL 746B
RTI, electrical, 120mil
140
°C
UL 746B
RTI, impact, 30mil
140
°C
UL 746B
RTI, impact, 60mil
140
°C
UL 746B
RTI, impact, 120mil
140
°C
UL 746B
RTI, strength, 30mil
140
°C
UL 746B
RTI, strength, 60mil
140
°C
UL 746B
RTI, strength, 120mil
140
°C
UL 746B
FLAMMABILITY
VALUE
UNIT
TEST NORM
Burning Behav. at 60mil nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
UL recognition
yes
-
UL 94
Burning Behav. at thickness h
HB
class
IEC 60695-11-10
Thickness tested
0.75
mm
IEC 60695-11-10
UL recognition
yes
-
UL 94
Oxygen index
20
%
ISO 4589-1/-2
Glow Wire Flammability Index, 80mil
750
°C
IEC 60695-2-12
Glow Wire Flammability Index, 120mil
850
°C
IEC 60695-2-12
Glow Wire Ignition Temperature, 120mil
825
°C
IEC 60695-2-13
Glow Wire Temperature, No Flame, 40mil
775
°C
IEC 60335-1
Glow Wire Temperature, No Flame, 60mil
775
°C
IEC 60335-1
Glow Wire Temperature, No Flame, 80mil
775
°C
IEC 60335-1
Glow Wire Temperature, No Flame, 120mil
850
°C
IEC 60335-1
FMVSS Class
B
-
ISO 3795 (FMVSS 302)
Burning rate, Thickness 1 mm
<80
mm/min
ISO 3795 (FMVSS 302)
ELECTRICAL PROPERTIES
VALUE
UNIT
TEST NORM
Relative permittivity, 100Hz
4.5
-
IEC 62631-2-1
Relative permittivity, 1MHz
4.4
-
IEC 62631-2-1
Dissipation factor, 100Hz
70
E-4
IEC 62631-2-1
Dissipation factor, 1MHz
110
E-4
IEC 62631-2-1
Volume resistivity
1E13
Ohm*m
IEC 62631-3-1
Surface resistivity
1E14
Ohm
IEC 62631-3-2
Electric strength
32
kV/mm
IEC 60243-1
Comparative tracking index
250
-
IEC 60112
Comparative tracking index
2
PLC
UL 746A
OTHER PROPERTIES
VALUE
UNIT
TEST NORM
Humidity absorption, 80mil
0.14
%
Sim. to ISO 62
Water absorption, 80mil
0.62
%
Sim. to ISO 62
Density
1690
kg/m3
ISO 1183
VDA PROPERTIES
VALUE
UNIT
TEST NORM
Fogging, G-value (condensate)
0
mg
ISO 6452
INJECTION
VALUE
UNIT
Drying Recommended
yes
Drying Temperature
120
°C
Drying Time, Dehumidified Dryer
4 - 6
h
Processing Moisture Content
≤0.021
%
Melt Temperature Optimum
285
°C
Min. melt temperature
280
°C
Max. melt temperature
300
°C
Max. screw tangential speed
0.2
m/s
Mold Temperature Optimum
120
°C
Min. mold temperature
110
°C
Max. mold temperature
1302
°C
Hold pressure range
≥80
MPa
Hold pressure time
4
s/mm
Back pressure
As low as possible
MPa
Ejection temperature
170
°C
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。