點擊圖片查看大圖CYCOLOY CS9610-111 防火PC/ABS 5VB阻燃等級
CYCOLOY CS9610 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is an excellent flammability, low smoke grade that can be injection molded. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VB flame rating. CYCOLOY CS9610 resin is an excellent candidate for a wide variety of applications including enclosures in public areas such as transportation.
CYCOLOY CS9610聚碳酸酯/丙烯腈-丁二烯-乙烯（PC/ABS）樹脂是一種優(yōu)良的阻燃性、低煙級的注塑成型樹脂。這種非氯化、非溴阻燃PC/ABS具有UL V0和5VB阻燃等級。CYCOLOY CS9610樹脂是一個很好的候選人，廣泛的應用，包括在公共領域，如運輸外殼。
CS9610物性表：
| REVISION: 27/05/2019 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| FLAME CHARACTERISTICS | 1) | |||
| UL Yellow Card | E207780-600276 | - | - | |
| UL Recognized, 94-5VB Flame Class Rating | ≥2 | mm | UL 94 | |
| UL Recognized, 94V-0 Flame Class Rating | ≥2 | mm | UL 94 | |
| NBS Smoke Density, Flaming, Dmax | 225 | - | ASTM E 662 | |
| NBS Smoke Density, Flaming, Ds 1.5 min | 40 | - | ASTM E 662 | |
| NBS Smoke Density, Flaming, Ds 4 min | 150 | - | ASTM E 662 | |
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 50 mm/min | 64 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 62 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 55 | % | ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 2600 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 98 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2440 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 50 mm/min | 62 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min | 50 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 4.8 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | >45 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 98 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 800 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 72 | J | ASTM D 3763 | |
| Izod Impact, notched 80*10*3 +23°C | 45 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 15 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 45 | kJ/m2 | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 15 | kJ/m2 | ISO 179/1eA | |
| THERMAL | ||||
| HDT, 0.45 MPa, 3.2 mm, unannealed | 118 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 105 | °C | ASTM D 648 | |
| Vicat Softening Temp, Rate B/50 | 124 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 127 | °C | ISO 306 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 106 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 1) | 90 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 1) | 90 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 1) | 90 | °C | UL 746B |
| PHYSICAL | ||||
| Specific Gravity | 1.2 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm | 0.4-0.6 | % | SABIC method | |
| Melt Flow Rate, 260°C/5.0 kgf | 15 | g/10 min | ASTM D 1238 | |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 12 | cm3/10 min | ISO 1133 | |
| INJECTION MOLDING | ||||
| Drying Temperature | 90 | °C | ||
| Drying Time | 4 | hrs | ||
| Maximum Moisture Content | 0.04 | % | ||
| Melt Temperature | 270-300 | °C | ||
| Nozzle Temperature | 265-300 | °C | ||
| Front - Zone 3 Temperature | 265-300 | °C | ||
| Middle - Zone 2 Temperature | 260-300 | °C | ||
| Rear - Zone 1 Temperature | 260-300 | °C | ||
| Hopper Temperature | 60-80 | °C | ||
| Mold Temperature | 60-90 | °C | ||
| Back Pressure | 0.3-0.7 | MPa | ||
| Screw Speed | 40-70 | rpm | ||
| Shot to Cylinder Size | 40-80 | % | ||
| Vent Depth | 0.038-0.076 | mm | ||