點擊圖片查看大圖LNP* THERMOCOMP* KB006 is a compound based on Acetal containing 30% Glass Bead.EUROPEASIAAMERICAS
LNP*THERMOCOMP*KB006是一種基于含有30%玻璃珠的縮醛的化合物。
PROPERTIES TYPICAL VALUES UNITS TEST METHODS MECHANICAL Tensile Stress, brk, Type I, 5 mm/min 34 MPa ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 19.8 % ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 43 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 3990 MPa ASTM D 790 Tensile Stress, break, 5 mm/min 37 MPa ISO 527 Tensile Strain, break, 5 mm/min 20.4 % ISO 527 Flexural Stress 65 MPa ISO 178 Flexural Modulus, 2 mm/min 4320 MPa ISO 178 IMPACT Izod Impact, unnotched, 23°C 374 J/m ASTM D 4812 Izod Impact, unnotched 80*10*4 +23°C 25 kJ/m2 ISO 180/1U Izod Impact, notched 80*10*4 +23°C 4 kJ/m2 ISO 180/1A THERMAL HDT, 0.45 MPa, 3.2 mm, unannealed 311 °C ASTM D 648 HDT, 1.82 MPa, 3.2mm, unannealed 218 °C ASTM D 648 CTE, -30°C to 30°C, flow 8.3E-05 1/°C ASTM D 696 CTE, -30°C to 30°C, xflow 8.3E-05 1/°C ASTM D 696 HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm 152 °C ISO 75/Bf HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 107 °C ISO 75/Af PHYSICAL Specific Gravity 1.64 - ASTM D 792 Moisture Absorption, 50% RH, 24 hrs 0.2 % ASTM D 570 Mold Shrinkage, flow, 24 hrs 1-3 % ASTM D 955 Mold Shrinkage, xflow, 24 hrs 1-3 % ASTM D 955 Density 1.64 g/cm3 ISO 1183 Moisture Absorption (23°C / 50% RH) 0.2 % ISO 62 INJECTION MOLDING Drying Temperature 80 °C Drying Time 4 hrs Melt Temperature 200-215 °C Front - Zone 3 Temperature 210-220 °C Middle - Zone 2 Temperature 195-205 °C Rear - Zone 1 Temperature 175-190 °C Mold Temperature 80-110 °C Back Pressure 0.2-0.3 MPa Screw Speed 30-60 rpm
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實性、準確性和合法性由發(fā)布企業(yè)負責(zé)，環(huán)球塑化網(wǎng)對此不承擔(dān)任何保證責(zé)任。我們原則上建議您優(yōu)先選擇“塑企通”會員合作! （2）同時我們鄭重提醒各位買/賣家，交易前請詳細核實對方身份，切勿隨意打款或發(fā)貨，謹防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請向環(huán)球塑化網(wǎng)舉報。
簡繁切換