長期供應(yīng)原裝PFA塑膠原料
NEOFLON? AP-230
全氟烷氧基
產(chǎn)品說明：
NEOFLON PFA is a copolymer of tetrafluoroethylene and perfluoroalkyl vinyl ether, NEOFLON PFA is a compound of carbon atoms and fluorine atoms in which a perfluoroalkoxy radical is bonded to the carbon chain in the following molecular structure.
NEOFLON PFA has better mechanical strength at high temperatures than NEOFLON FEP, and has excellent moldability for easy of processing by extrusion, compression, blow, transfer, and injection molding methods. Due to the high bonding strength of the carbon, fluorine and oxygen atoms, NEOFLON PFA demonstrates nearly the same outstanding capabilities as PTFE in temperatures ranging -200°C ~+260°C. NEOFLON PFA has excellent transparency for use in melt-flow processing.
NEOFLON? AP-230 物性表
|
基本信息
|
|
|
特性
|
-
低摩擦系數(shù)
-
高溫強(qiáng)度
-
共聚物
-
良好的成型性能
-
良好的電氣性能
-
良好的抗腐蝕性
-
耐氣候影響性能良好
-
清晰度，高
-
阻燃性
|
|
用途
|
|
|
外觀
|
|
|
形式
|
|
|
加工方法
|
|
|
物理性能
|
額定值
|
單位制
|
測試方法
|
|
比重
|
2.14 到 2.16
|
g/cm3
|
ASTM D792
|
|
表觀密度
|
1.00 到 1.40
|
g/cm3
|
JIS K6891
|
|
熔流率（熔體流動速率）?(372°C/5.0 kg)
|
1.5 到 2.5
|
g/10 min
|
ASTM D1238
|
|
吸水率?(飽和)
|
< 0.010
|
%
|
ASTM D570
|
|
硬度
|
額定值
|
單位制
|
測試方法
|
|
肖氏硬度?(邵氏 D)
|
60 到 70
|
|
ASTM D2240
|
|
機(jī)械性能
|
額定值
|
單位制
|
測試方法
|
|
抗張強(qiáng)度?(屈服)
|
30.4 到 34.3
|
MPa
|
JIS K6891
|
|
伸長率?(斷裂)
|
300 到 400
|
%
|
JIS K6891
|
|
彎曲模量
|
580 到 690
|
MPa
|
ASTM D790
|
|
壓縮模量
|
490 到 590
|
MPa
|
ASTM D695
|
|
壓縮強(qiáng)度
|
|
|
ASTM D695
|
|
????1% 應(yīng)變
|
4.90 到 5.90
|
MPa
|
ASTM D695
|
|
????25% 應(yīng)變
|
31.4 到 33.3
|
MPa
|
ASTM D695
|
|
摩擦系數(shù)?(與鋼 - 靜態(tài))
|
0.040 到 0.050
|
|
ASTM D1894
|
|
負(fù)載變形
|
|
|
ASTM D621
|
|
????25°C, 14 MPa?1
|
8.00 到 9.00
|
%
|
ASTM D621
|
|
????25°C, 14 MPa?2
|
2.50 到 3.00
|
%
|
ASTM D621
|
|
????100°C, 6.9 MPa?3
|
8.50 到 9.50
|
%
|
ASTM D621
|
|
????100°C, 6.9 MPa?4
|
2.00 到 3.00
|
%
|
ASTM D621
|
|
Flexural Strength
|
No break
|
|
ASTM D790
|
|
沖擊性能
|
額定值
|
單位制
|
測試方法
|
|
懸壁梁缺口沖擊強(qiáng)度
|
無斷裂
|
|
ASTM D256
|
|
熱性能
|
額定值
|
單位制
|
測試方法
|
|
熔融溫度
|
300 到 310
|
°C
|
ASTM D4591
|
|
線形熱膨脹系數(shù) - 流動?(20 到 100°C)
|
1.2E-4
|
cm/cm/°C
|
ASTM D696
|
|
比熱
|
1050
|
J/kg/°C
|
|
|
導(dǎo)熱系數(shù)
|
0.26
|
W/m/K
|
ASTM C177
|
|
可燃性
|
額定值
|
單位制
|
測試方法
|
|
UL 阻燃等級?(1.57 mm)
|
V-0
|
|
UL 94
|
|
極限氧指數(shù)?(1.57 mm)
|
> 95
|
%
|
ASTM D2863
|
|
充模分析
|
額定值
|
單位制
|
|
|
熔體粘度?(380°C)
|
2.00E+6 到 2.50E+7
|
mPa·s
|
|
|
備注
|
|
1 .
|
Total deformation
|
|
2 .
|
Compressive creep
|
|
3 .
|
Total deformation
|
|
4 .
|
Compressive creep
|
點(diǎn)擊圖片查看大圖