| NORYL GTX? Resin | ||
| Grades |
De |
|
| GTX4610 |
PPE+PA, Glass, Datasheet Product Data: Auto Data: |
|
| GTX673 |
PPE+PA, Conductive, Datasheet Product Data: Auto Data: |
|
| GTX678 |
PPE+PA, Flame Retardant, Conductive, Heat Stabilized, Impact Modified, Nonhalogenated, Datasheet Product Data: Auto Data: |
|
| GTX8730 |
PPE+PA, Glass, Conductive, Datasheet Product Data: Auto Data: |
|
| GTX902D |
NORYL GTX902D is a GTX902E with smaller shaped pellets. Datasheet Product Data: Auto Data: |
|
| GTX975 |
18% mineral filled conductive NORYL GTX. Datasheet Product Data: Auto Data: |
|
| GTX989 |
PPE+PA, Conductive, High Impact, Datasheet Product Data: Auto Data: Auto Specification |
|
| NX0031 |
PPE+PA, conductive with high impact Datasheet Product Data: Auto Data: |
|
NORYL GTX ? Resin GTX4610 |
SI | | British | | Metric | Americas: COMMERCIAL |
| NORYL GTX GTX4610 resin is a high performance, 10% glass filled blend of PPE/PA that exhibits an excellent balance of non-halogenated flame retardance, dimensional stability, high heat resistance, strength, and flow. The material is available in limited colors for injection molding. |
|
Property |
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 5 mm/min | 890 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 890 | kgf/cm2 | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 50900 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 1470 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 46900 | kgf/cm2 | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 88 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 88 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 5000 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 145 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 4600 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C | 8 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, notched, -30°C | 6 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 122 | cm-kgf | ASTM D 3763 | |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m2 | ISO 179/1eA | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 | 218 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 4.1E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 7.4E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 4.1E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 | |
| Vicat Softening Temp, Rate B/50 | 218 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 220 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 224 | °C | ISO 75/Bf | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.21 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.88 - 0.94 | % | SABIC Method | |
| Mold Shrinkage, xflow, 3.2 mm (5) | 0.95 - 1.01 | % | SABIC Method | |
| Melt Flow Rate, 300°C/5.0 kgf | 18 | g/10 min | ASTM D 1238 | |
| Density | 1.21 | g/cm3 | ISO 1183 | |
| Water Absorption, (23°C/sat) | 3.8 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.5 | % | ISO 62 | |
| Melt Volume Rate, MVR at 300°C/5.0 kg | 15 | cm3/10 min | ISO 1133 | |
| ELECTRICAL | Value | Unit | Standard | |
| Volume Resistivity | 1.E+16 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in air, 1.6 mm | 23.2 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 24.4 | kV/mm | ASTM D 149 | |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 1 | PLC Code | UL 746A | |
| Comparative Tracking Index | 425 | V | IEC 60112 | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Compliant, 94V-1 Flame Class Rating (3)(4) | 0.8 | mm | UL 94 by SABIC-IP | |
| UL Compliant, 94-5VA Rating (3)(4) | 2 | mm | UL 94 by SABIC-IP | |
| UL Compliant, 94-5VB Rating (3)(4) | 2 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 960°C, passes at | 2 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 825 | °C | IEC 60695-2-13 | |
| Source GMD, last updated:2013/03/04 |
|
Processing |
| ? Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 95 - 105 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.07 | % |
| Minimum Moisture Content | 0.02 | % |
| Melt Temperature | 280 - 305 | °C |
| Nozzle Temperature | 280 - 305 | °C |
| Front - Zone 3 Temperature | 275 - 305 | °C |
| Middle - Zone 2 Temperature | 270 - 305 | °C |
| Rear - Zone 1 Temperature | 265 - 305 | °C |
| Mold Temperature | 75 - 120 | °C |
| Back Pressure | 0.3 - 1.4 | MPa |
| Screw Speed | 20 - 100 | rpm |
| Shot to Cylinder Size | 30 - 50 | % |
| Vent Depth | 0.013 - 0.038 | mm |
| Source GMD, last updated:2013/03/04 |
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。