| LNP? LUBRICOMP Compound | ||
| Grades |
De |
|
| LCL33 |
Wear Resistant, Polyetheretherketone, PTFE, Carbon Fiber Datasheet Product Data: Auto Data: |
|
| LCL33E |
Easy Molding, Polyetheretherketone, Carbon Fiber, PTFE, Wear Resistant Datasheet Product Data: Auto Data: |
|
| LCL33EXQ |
Polyetheretherketone, Carbon Fiber, PTFE, Wear Resistant, Easy Molding Datasheet Product Data: Auto Data: |
|
| LCL36E |
PEEK, Carbon Fiber, PTFE, Wear Resistant Datasheet Product Data: Auto Data: |
|
| LFL36E |
Polyetheretherketone, Glass Fiber, PTFE, Easy Molding, Wear Resistant Datasheet Product Data: Auto Data: |
|
| LGL33 |
Polyetheretherketone, Graphite, PTFE, Wear Resistant Datasheet Product Data: Auto Data: |
|
| LL002 |
Polyetheretherketone, PTFE, Wear Resistant Datasheet Product Data: Auto Data: |
|
| LL003 |
Polyetheretherketone, PTFE, Wear Resistant Datasheet Product Data: Auto Data: |
|
| LL004 |
Wear Resistant, Polyetheretherketone, PTFE Datasheet Product Data: Auto Data: |
|
| LL004C |
Wear Resistant, Clean Compounding System, Polyetheretherketone, PTFE Datasheet Product Data: Auto Data: |
|
| LX00430 |
PEEK, Proprietary Filler(s), Wear Resistant Datasheet Product Data: Auto Data: |
|
| LX91475 |
Easy Molding, Polyetheretherketone High Temperature Bearing Grade, Wear Resistant Datasheet Product Data: Auto Data: |
|
LNP?LUBRICOMP? Compound LX91475 |
SI | | British | | Metric | Americas: COMMERCIAL |
| Also known as:LNP?LUBRICOMP?Compound LTW |
| Product reorder name:LX91475 |
| LNP LUBRICOMP LX91475 is a compound based on Polyetheretherketone resin containing proprietary fillers. Added features of this material include: Easy Molding, High Temperature Bearing Grade, Wear Resistant. |
|
Property |
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 5 mm/min | 1640 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 1620 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 2.1 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 126000 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 2430 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 105000 | kgf/cm2 | ASTM D 790 | |
| Tensile Stress, break, 5 mm/min | 160 | MPa | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 2.1 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 11870 | MPa | ISO 527 | |
| Flexural Stress | 229 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 10320 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, unnotched, 23°C | 49 | cm-kgf/cm | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 5 | cm-kgf/cm | ASTM D 256 | |
| Multiaxial Impact | 20 | cm-kgf | ISO 6603 | |
| Instrumented Impact Total Energy, 23°C | 71 | cm-kgf | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m2 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A | |
| THERMAL | Value | Unit | Standard | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 336 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 322 | °C | ASTM D 648 | |
| CTE, -30°C to 30°C, flow | 1.8E-05 | 1/°C | ASTM D 696 | |
| CTE, -30°C to 30°C, xflow | 4.2E-05 | 1/°C | ASTM D 696 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 335 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 335 | °C | ISO 75/Af | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.4 | - | ASTM D 792 | |
| Density | 1.43 | g/cm3 | ASTM D 792 | |
| Moisture Absorption, 50% RH, 24 hrs | 0.05 | % | ASTM D 570 | |
| Mold Shrinkage, flow, 24 hrs (5) | 0.4 - 0.6 | % | ASTM D 955 | |
| Mold Shrinkage, xflow, 24 hrs (5) | 0.7 - 0.9 | % | ASTM D 955 | |
| Wear Factor Washer | 16 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified | |
| Wear Factor Ring | 2 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified | |
| Dynamic COF | 0.34 | - | ASTM D 3702 Modified | |
| Static COF | 0.42 | - | ASTM D 3702 Modified | |
| Moisture Absorption (23°C / 50% RH) | 0.08 | % | ISO 62 | |
| Source GMD, last updated:2013/12/30 |
|
Processing |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | hrs |
| Front - Zone 3 Temperature | 380 - 400 | °C |
| Middle - Zone 2 Temperature | 380 - 400 | °C |
| Rear - Zone 1 Temperature | 370 - 380 | °C |
| Mold Temperature | 175 - 190 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 60 - 100 | rpm |
| Source GMD, last updated:2013/12/30 |
|
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. |
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。