點(diǎn)擊圖片查看大圖
|
性能特點(diǎn)
|
|
|||
|
用途
|
|
|||
|
外觀
|
|
|||
|
形式
|
|
|||
|
加工方法
|
|
| 物理性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
比重
|
|||
|
--
|
1.27
|
g/cm³
|
ASTM D792, ASTM D1505 |
|
23°C
|
1.27
|
g/cm³
|
ISO 1183/D |
|
吸水率 (23°C, 24 hr)
|
0.13
|
%
|
ASTM D570, ISO 62 |
| 硬度 |
額定值
|
單位制
|
測(cè)試方法
|
|
洛氏硬度
|
|||
|
R 計(jì)秤, 23°C
|
106
|
ASTM D785 | |
|
R 計(jì)秤, 23°C
|
109
|
ISO 2039-2 |
| 機(jī)械性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
拉伸模量 (23°C)
|
2100
|
MPa
|
ASTM D638, ISO 527-2 |
|
抗張強(qiáng)度
|
ASTM D638, ISO 527-2 | ||
|
屈服, 23°C
|
50.0
|
MPa
|
|
|
斷裂, 23°C
|
28.0
|
MPa
|
|
|
伸長(zhǎng)率
|
|||
|
斷裂, 23°C
|
130
|
%
|
ASTM D638 |
|
斷裂, 23°C
|
100
|
%
|
ISO 527-2 |
|
彎曲模量
|
|||
|
23°C
|
2100
|
MPa
|
ASTM D790 |
|
23°C
|
2000
|
MPa
|
ISO 178 |
|
彎曲強(qiáng)度
|
|||
|
23°C
|
68.0
|
MPa
|
ISO 178 |
|
屈服, 23°C
|
70.0
|
MPa
|
ASTM D790 |
|
撕裂阻力
|
ASTM D2582 | ||
|
MD : 23°C, 250.0 µm
|
93
|
N
|
|
|
TD : 23°C, 250.0 µm
|
93
|
N
|
|
| 薄膜 |
額定值
|
單位制
|
測(cè)試方法
|
|
薄膜厚度 - 經(jīng)測(cè)試
|
250
|
µm
|
|
|
割線模量
|
ASTM D882 | ||
|
MD : 250 µm
|
1900
|
MPa
|
|
|
TD : 250 µm
|
1900
|
MPa
|
|
|
抗張強(qiáng)度
|
ASTM D882 | ||
|
MD : 屈服, 250 µm
|
52.0
|
MPa
|
|
|
TD : 屈服, 250 µm
|
52.0
|
MPa
|
|
|
MD : 斷裂, 250 µm
|
59.0
|
MPa
|
|
|
TD : 斷裂, 250 µm
|
55.0
|
MPa
|
|
|
伸長(zhǎng)率
|
ASTM D882 | ||
|
MD : 屈服, 250 µm
|
4.0
|
%
|
|
|
TD : 屈服, 250 µm
|
4.0
|
%
|
|
|
MD : 斷裂, 250 µm
|
400
|
%
|
|
|
TD : 斷裂, 250 µm
|
400
|
%
|
|
|
落錘沖擊 3
|
ASTM D1709A | ||
|
-18°C, 250 µm
|
500
|
g
|
|
|
23°C, 250 µm
|
400
|
g
|
|
|
埃爾曼多夫抗撕強(qiáng)度
|
ASTM D1922 | ||
|
MD : 250 µm
|
1400
|
g
|
|
|
TD : 250 µm
|
1700
|
g
|
|
|
褲型撕裂耐性 4
|
ISO 6383-1 | ||
|
MD
|
36.0
|
N/mm
|
|
|
TD
|
36.0
|
N/mm
|
|
|
透氧率 (23°C, 250 µm, 50% RH)
|
10
|
cm³·mm/m²/atm/24 hr
|
ASTM D3985 |
|
水氣透過(guò)率 (38°C, 250 µm, RH)
|
7.0
|
g/m²/24 hr
|
ASTM F1249 |
|
Carbon Dioxide Permeability (23°C, 250.0 µm)
|
49
|
cm³·mm/m²/atm/24 hr
|
ASTM D1434 |
|
Tear Propagation Resistance 5
|
ASTM D1938 | ||
|
MD : 23°C, 250.0 µm
|
36
|
kN/m
|
|
|
TD : 23°C, 250.0 µm
|
36
|
kN/m
|
|
| 沖擊性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
懸壁梁缺口沖擊強(qiáng)度
|
|||
|
-40°C
|
37
|
J/m
|
ASTM D256 |
|
23°C
|
100
|
J/m
|
ASTM D256 |
|
-40°C
|
4.2
|
kJ/m²
|
ISO 180/1A |
|
23°C
|
6.2
|
kJ/m²
|
ISO 180/1A |
|
無(wú)缺口懸臂梁沖擊
|
|||
|
-40°C, 3.20 mm
|
無(wú)斷裂
|
ASTM D4218 | |
|
-30°C, 3.20 mm
|
無(wú)斷裂
|
ASTM D4218 | |
|
-20°C, 3.20 mm
|
無(wú)斷裂
|
ASTM D4218 | |
|
23°C, 3.20 mm
|
無(wú)斷裂
|
ASTM D4218 | |
|
-40°C 6
|
無(wú)斷裂
|
ISO 180/1U | |
|
-30°C 6
|
無(wú)斷裂
|
ISO 180/1U | |
|
-20°C 6
|
無(wú)斷裂
|
ISO 180/1U | |
|
23°C 6
|
無(wú)斷裂
|
ISO 180/1U | |
|
裝有測(cè)量?jī)x表的落鏢沖擊
|
|||
|
-40°C, 2.50 mm, Energy at Peak Load
|
41.0
|
J
|
ASTM D3763 |
|
-40°C, 3.20 mm, Energy at Peak Load
|
50.0
|
J
|
ASTM D3763 |
|
23°C, 2.50 mm, Energy at Peak Load
|
28.0
|
J
|
ASTM D3763 |
|
23°C, 3.20 mm, Energy at Peak Load
|
33.0
|
J
|
ASTM D3763 |
|
-40°C, 2.50 mm, 能量到力量峰值 7, 8
|
35.0
|
J
|
ISO 6603-2 |
|
-40°C, 3.20 mm, 能量到力量峰值 7, 8
|
36.0
|
J
|
ISO 6603-2 |
|
23°C, 2.50 mm, 能量到力量峰值 7, 8
|
40.0
|
J
|
ISO 6603-2 |
|
23°C, 3.20 mm, 能量到力量峰值 7, 8
|
44.0
|
J
|
ISO 6603-2 |
| 熱性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
熱變形溫度
|
ASTM D648 | ||
|
0.45 MPa, 未退火
|
70.0
|
°C
|
|
|
1.8 MPa, 未退火
|
64.0
|
°C
|
|
|
玻璃轉(zhuǎn)化溫度(DSC)
|
80.0
|
°C
|
DSC |
|
維卡軟化溫度
|
85.0
|
°C
|
ASTM D1525 |
|
線形膨脹系數(shù) - 流動(dòng) (-30 到 40°C)
|
0.000051
|
cm/cm/°C
|
ASTM D696 |
|
比熱
|
DSC | ||
|
60°C
|
1300
|
J/kg/°C
|
|
|
100°C
|
1760
|
J/kg/°C
|
|
|
150°C
|
1880
|
J/kg/°C
|
|
|
200°C
|
1970
|
J/kg/°C
|
|
|
250°C
|
2050
|
J/kg/°C
|
|
|
導(dǎo)熱系數(shù) (23°C)
|
0.21
|
W/m/K
|
ASTM C177 |
| 電氣性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
介電強(qiáng)度 9 (23°C)
|
16
|
kV/mm
|
ASTM D149 |
|
介電常數(shù)
|
ASTM D150 | ||
|
23°C, 1 kHz
|
2.60
|
||
|
23°C, 1 MHz
|
2.40
|
||
|
耗散因數(shù)
|
ASTM D150 | ||
|
23°C, 1 kHz
|
0.0050
|
||
|
23°C, 1 MHz
|
0.020
|
||
|
耐電弧性
|
158
|
sec
|
ASTM D495 |
| 光學(xué)性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
光澤度 (45°, 250 µm)
|
108
|
ASTM D2457 | |
|
透射率
|
ASTM D1003 | ||
|
常規(guī), 250 µm
|
89.0
|
%
|
|
|
總計(jì), 250 µm
|
91.0
|
%
|
|
|
透明度 (250 µm)
|
85.0
|
ASTM D1746 | |
|
霧度 (250 µm)
|
0.80
|
%
|
ASTM D1003 |
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。