注塑工藝：
Processing Texts
Injection molding
PREPROCESSING
Drying recommended = Yes, if moisture content of resin exceeds recommended level
Drying temperature = 80°C
Drying time, dehumidified dryer = 2-4 h
Processing moisture content = <0.2 %
PROCESSING
Melt temperature optimum = 290°C
Melt temperature range = 280-300°C
Mould temperature optimum = 100°C
Mould temperature range = 70-120°C
Drying recommended = Yes, if moisture content of resin exceeds recommended level
Drying temperature = 80°C
Drying time, dehumidified dryer = 2-4 h
Processing moisture content = <0.2 %
PROCESSING
Melt temperature optimum = 290°C
Melt temperature range = 280-300°C
Mould temperature optimum = 100°C
Mould temperature range = 70-120°C
| Rheological properties | dry / cond | Unit | Test Standard | |
| Viscosity number | 130 / * | cm³/g | ISO 307, 1157, 1628 | |
| Moulding shrinkage, parallel | 0.3 / * | % | ISO 294-4, 2577 | |
| Moulding shrinkage, normal | 0.7 / * | % | ISO 294-4, 2577 |
| Mechanical properties | dry / cond | Unit | Test Standard | |
| Tensile Modulus | 8800 / 7800 | MPa | ISO 527-1/-2 | |
| Stress at break | 145 / 110 | MPa | ISO 527-1/-2 | |
| Strain at break | 2.5 / 2.6 | % | ISO 527-1/-2 | |
| Tensile creep modulus | ISO 899-1 | |||
| 1h | * / 7000 | MPa | ||
| 1000h | * / 6000 | MPa | ||
| Charpy impact strength | ISO 179/1eU | |||
| 23°C | 41 / 41 | kJ/m² | ||
| -30°C | 40 / 40 | kJ/m² | ||
| Charpy notched impact strength | ISO 179/1eA | |||
| 23°C | 4 / 4 | kJ/m² | ||
| -30°C | 4 / 3 | kJ/m² |
| Thermal properties | dry / cond | Unit | Test Standard | |
| Melting temperature, 10°C/min | 245 / * | °C | ISO 11357-1/-3 | |
| Glass transition temperature, 10°C/min | 90 / - | °C | ISO 11357-1/-2 | |
| Temp. of deflection under load, 1.8 MPa | 230 / * | °C | ISO 75-1/-2 | |
| Coeff. of linear therm. expansion, parallel | 23 / * | E-6/K | ISO 11359-1/-2 | |
| Coeff. of linear therm. expansion, normal | 60 / * | E-6/K | ISO 11359-1/-2 | |
| Thermal conductivity of melt | 0.26 | W/(m K) | - | |
| Spec. heat capacity of melt | 2280 | J/(kg K) | - |
| Flammability | dry / cond | Unit | Test Standard | |
| Burning Behav. at 1.5mm nom. thickn. | HB / * | class | IEC 60695-11-10 | |
| Thickness tested | 1.5 / * | mm | IEC 60695-11-10 |
| Electrical properties | dry / cond | Unit | Test Standard | |
| Volume resistivity | 8E12 / 2E10 | Ohm*m | IEC 60093 | |
| Surface resistivity | * / 3E14 | Ohm | IEC 60093 | |
| Electric strength | 41 / 41 | kV/mm | IEC 60243-1 |
| Other properties | dry / cond | Unit | Test Standard | |
| Humidity absorption, 2mm | 1.5 / * | % | Sim. to ISO 62 | |
| Water absorption, 2mm | 5 / * | % | Sim. to ISO 62 | |
| Density | 1460 / - | kg/m³ | ISO 1183 | |
| Density of melt | 1300 | kg/m³ | - |
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。